Galvanized Power Transmission Electrical Steel Tubular Tower Pole details below

Height  From 10M-100M or according to client’s requirement
Suit forElectric Power Transmission and Distribution
ShapePolygonal or Conical
MaterialNormally Q235B/A36,Yeild Strength≥235MPa
Q345B/A572,Yeild Strength≥345MPa
As well as Hot Rolled coil from ASTM572, GR65,GR50,SS400
Power Capacity10kV to 500kV
Tolerance of the dimensionAccording to client’s requirement
Surface treatmentHot-dip-galvanized following ASTM123, or any other standard by client’s requirement
Joint of PolesSlip joint, flanged connected
Length of per sectionWithin 13M once forming
Welding StandardAWS(American Welding Society)D 1.1
Production ProcessRaw material test-cutting-bending-welding-dimension verify-flange welding-hole drilling-sample assemble-surface clean-galvanization or power coating /painting-recalibration-packages
PackagesPacking with plastic paper or according to client’s requirement
Life PeriodMore than 25 years, it is according to installing environment

Electric Pole Machine Manufacturing progress:

Raw Material :When purchasing the raw material (steel plate), on sheet of mill certificate from mill factory must be enclosed. When the raw material arrives at the warehouse, the quality department must take the elongation test and the chemical composition analysis to make sure the raw material have meet all the standard that the needed before production.

Plasma Cutting:Cuting the raw material that have meet all the standard required into different length and width. CNC laser cutting is used to direct the material or the laser beam generated. A typical commercial laser for cutting materials would involve a motion control system to follow a CNC or G-code of the pattern to be cut onto the material. The focused laser beam is directed at the material, which then either melts, burns, vaporizes away, or is blown away by a jet of gas, leaving an edge with a high-quality surface finish.

Bending:Forming the cutted steel plate into the shape (circular or polygonal or other shape ) that as per specified in the drawing. This invention relates to forming devices and more particularly to devices or machines for bending longitudinally rolled sections or strips of metal stock to desired curvilinear shapes.

Welding:After molding, weld the steel plate together. Usually it is longitudinal welds. It adopts A.C.inverter control, with functions of stable running and fast traveling speed; The seam-tracking arc-guide mechanism is three-spindle system to guarantee the alignment without aberrancy; The main frame and welding machine are intergrated control, with flux auto-recovering system and it is easy to operate with high efficiency.